Organic/inorganic multi-layered gas barrier film

ABSTRACT

The present invention employs the totally printable process to fabricate an organic/inorganic multi-layered laminate gas barrier film. Such totally printable process is simple with lower costs. Moreover, through the pattern design, the adhesion between the organic and inorganic layers is improved.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the priority benefit of U.S. Provisional Application Ser. No. 61/122,414, filed on Dec. 15, 2008. The entirety of the above-mentioned patent application is hereby incorporated by reference herein and made a part of this specification.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention generally relates to a barrier film and a manufacturing method thereof. More particularly, the present invention relates to an organic/inorganic multi-layered gas barrier film and a manufacturing method thereof.

2. Description of Related Art

As the flexible substrates afford better pliability and design freedom, the flexible display panels become popular and thus quickly replace the rigid display panels. Compared with the rigid substrates, the flexible plastic substrates are cheaper, compatible with workability and safety requirements and suitable for display medium and roll-to-roll processes. However, certain drawbacks exist, including low temperature and chemical resistance, high permeability to oxygen and water vapour and large thermal expansion coefficients. Typical flexible plastic substrate has water permeation of 100˜10 g/m²/day (at 25° C.), which is unable to completely prevent water vapour and oxygen permeation, thus leading to device impairment. In order to avoid water vapour and oxygen permeation, specific material is coated between the plastic substrate and the electronic devices. Such tight-sealing barrier material has to be defect-free and pinhole-free when formed as a membrane or a film, and highly transparent or no absorption to visible light. Such material can be formed as a single-layered or multilayered laminate film for gas barrier purposes.

Flexible gas barrier films include inorganic layers (of metal oxides, metal nitrides or metal oxynitrides) and organic layers. The inorganic layers provide better gas barrier capability, while the organic layers can help maintain the flexibility of the barrier film. However, conventional gas barrier structures are mainly fabricated by alternatively laminating organic/inorganic films, but the adhesion between the organic material and the inorganic material is poor. If further treatment is performed to the surface(s) of the organic or inorganic layers for improving the adhesion there-between, the production cost will be increased. Also certain defects, such as pinholes, exist in the barrier films fabricated by the vacuum processes and cause the permeation of the oxygen and water vapour, leading to degradation of the electronic device and shorter life time. Further shortcomings include high-priced apparatus or systems for the vacuum processes, low yields and difficulties in fabrication of large-sized substrates.

SUMMARY OF THE INVENTION

The present invention is directed to a manufacturing process for forming a multi-layered gas barrier laminate film, which is simple and straightforward.

The present invention provides a total printable process for forming a multi-layered gas barrier laminate film by alternately forming organic layers and inorganic layers, which can help reduce the formation of pinholes.

The present invention provides a multi-layered gas barrier laminate film, comprising a flexible substrate, a plurality of organic layers disposed over the flexible substrate and a plurality of inorganic layers disposed over the flexible substrate. The organic layers and the inorganic layers are stacked in alternation, and the inorganic layers are interconnected with one another.

According to embodiments of the present invention, each of the plurality of organic layers has a pattern, and the patterns of the most adjacent two organic layers are off-set or not aligned. In this case, due to the off-set pattern designs, the inorganic material within the barrier film is three-dimensionally interconnected, and the organic material is sandwiched between the inorganic material, which improves the flexibility of the barrier film and avoids possible cracking of the barrier film.

In order to make the above and other features and advantages of the present invention more comprehensible, embodiments accompanied with figures are described in detail below.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.

FIGS. 1A-1C describes the exemplary processes of forming an organic layer and then an inorganic layer for a barrier film according to the present invention.

FIG. 2A is a schematic cross-sectional view illustrating the barrier film according to an embodiment of the present invention.

FIG. 2B is an exemplary top view of the barrier film according to an embodiment of the present invention.

FIGS. 3A-3B describes the exemplary processes of forming a mixture layer for a barrier film according to the present invention.

DESCRIPTION OF THE EMBODIMENTS

Reference will now be made in detail to the present preferred embodiments of the invention, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers are used in the drawings and the descriptions to refer to the same or like parts.

FIGS. 1A-1C describes the exemplary processes of forming an organic layer and then an inorganic layer for a barrier film according to the present invention. Following the process flow of FIG. 1A, a plastic substrate 100 is provided (Step 10 a). Later, with the screen plate P, a patterned organic layer 110 (with a pattern defined by the openings S) is coated on the surface 100 a of the plastic substrate 100 (Step 10 b) by screen printing, for example. Subsequently an inorganic layer 120 is coated to the patterned organic layer 110, filling up the openings S of the patterned organic layer 110 and covering the whole surface of the patterned organic layer 110 (Step 10 c), by roller printing, for example. Afterwards, a drying step (Step 10 d) is performed to dry up the inorganic layer 120. The drying step can includes a UV-dried step, a thermal-dried step, an air-dried step and/or an electron-bean irradiation step. Such process flow can be repeated several times to form several organic layers and several inorganic layers laminated in alternation, depending on the gas barrier capability required by the products in process.

Following the process flow of FIG. 1B, a plastic substrate 100 is provided and an organic material 11 is provided to a template 12 with a pattern (Step 10 a). Later, a patterned organic layer 110 is formed on the plastic substrate 100 after transferring the organic material 11 from the template 12 to the plastic substrate 100 by micro-imprinting (micro-stamping), for example (Step 10 b). Subsequently an inorganic layer 120 is coated to the patterned organic layer 110, filling up the openings S of the patterned organic layer 110 and covering the whole surface of the patterned organic layer 110 (Step 10 c), by Doctor blade coating or squeegee printing, for example. Afterwards, a drying step (Step 10 d) is performed to dry up the inorganic layer 120. The drying step can includes a UV-dried step, a thermal-dried step, an air-dried step and/or an electron-bean irradiation step. Such process flow can be repeated several times to form several organic layers and several inorganic layers laminated in alternation, depending on the gas barrier capability required by the products in process.

Following the process flow of FIG. 1C, a plastic substrate 100 is provided and an organic layer 110 a is formed on the plastic substrate 100 by, for example, spin coating (Step 10 a). Later, the organic layer 110 a is patterned by photolithography and wet-etching to form a patterned organic layer 110 on the plastic substrate 100 (Step 10 b). Subsequently an inorganic layer 120 is coated to the patterned organic layer 110, filling up the openings S of the patterned organic layer 110 and covering the whole surface of the patterned organic layer 110 (Step 10 c), by doctor blade coating or squeegee printing, for example. Afterwards, a drying step (Step 10 d) is performed to dry up the inorganic layer 120. The drying step can includes a UV-dried step, a thermal-dried step, an air-dried step and/or an electron-bean irradiation step. Such process flow can be repeated several times to form several organic layers and several inorganic layers laminated in alternation, depending on the gas barrier capability required by the products in process.

Preferably, either the organic layer or the inorganic layer of the present invention is formed by the so-called totally printable process. The totally printable process may include screen printing technology, doctor blade coating (without the screen plate), squeegee printing, roll coating, micro (or nano)-imprinting, spray printing, spin coating, flow coating, capillary coating, chemical coating and dip or immersion coating. Such totally printable process is simple, low-cost and is able to form a single layer with pattern (or without pattern) in one step. Due to the lamination of the organic layer(s) and the inorganic layer(s), the pinholes of the previously-formed layer can be greatly reduced or compensated by the fluidity of the later-formed layer.

The material of the plastic substrate can be polyethylene terephthalate (PET), polycarbonate (PC), polymethylmethacrylate (PMMA), polyvinylchloride (PVC), polyimide (PI) or polyethylene (PE), for example.

The organic material suitable for the above processes can be macromolecules or polymers with low film-forming temperature and high light transparency, such as, optical grade polymethylmethacrylate (PMMA), poly-p-xylene, poly-p-xylene, ethylene-chlorotrifluoroethylene copolymer, fluorinated ethylene-propylene, fluorinated ethers, polytetrafluoroethene, polychlorotrifluoroethylene, polyimide precursors, self-assembly materials or light sensitive materials. The organic material may further includes absorbent or desiccant additives, such as NaBH₄, CaCl₂, silica gel, and CaO. The organic material may further include nano-particles of aluminium oxide, zinc oxide or silver, for increasing the barrier capability.

The inorganic material suitable for the above process can be sol-gel materials of gas barrier capability, silicon oxide or metal oxides, such as titanium oxide, tin oxide, aluminium oxide or zinc oxide.

The organic material used for the organic layer can be the same or different between layers. Similarly, the inorganic material used for the inorganic layer can be the same or different between layers.

FIG. 2A is a schematic cross-sectional view illustrating the barrier film according to an embodiment of the present invention, while FIG. 2B is an exemplary top view of the barrier film.

In FIG. 2A, three layers of patterned organic layers 210 a, 210 b and 210 c and three layers of inorganic layers 220 a, 220 b and 220 c are stacked in alternation and disposed on the substrate 200. Within the laminate film 20, the inorganic layers 220 a/220 b/220 c are interconnected with one another and become a continuous matrix structure. Due to the patterned organic layer formed by printing process, the inorganic material within the laminate film is interconnected and becomes continuous throughout layers for better gas barrier efficiency. Hence, the adhesion between the organic and inorganic layers is increased and peeling between the organic and inorganic layers is decreased.

From FIG. 2B, the patterned organic layers 210 a, 210 b and 210 c are shown as round blocks arranged in stagger. However, the shape or design of the pattern of the organic layer is not limited by the embodiments provided herein. Preferably, the patterns of the most adjacent two organic layers are staggered or complement to each other. At least, the patterns of the most two adjacent two organic layers are not aligned or are off-set. In this case, due to the off-set pattern designs, in the vertical direction of the barrier film, the inorganic material within the barrier film is not directly piled on each other, and the organic material is sandwiched between the inorganic material, which improves the flexibility of the barrier film and avoids possible cracking of the barrier film.

Macroscopically, the inorganic material within the laminate film can be regard as an interconnected matrix or web structure, while the unconnected organic material distributed within the continuous inorganic material can help enhance the pliability and flexibility of the laminate film.

Conventionally, in order to enhance gas barrier capability, the thickness of the inorganic layer needs to be increased or more inorganic layers are required. But the thicker the inorganic layer, more fragile the inorganic layer is, when outer force is applied. However, due to the off-set pattern arrangement between the layers, the thickness of the inorganic layers is not diametrically accumulated but the permeation pathway for water or oxygen gas becomes meandering and is extended in this regard.

In addition to the exemplary processes of forming an organic layer and then an inorganic layer for the barrier film, an organic/inorganic hybrid layer can be formed after forming the organic layer and before forming the inorganic layer. FIGS. 3A-3B describes the exemplary processes of forming a mixture layer for a barrier film according to the present invention.

Following the process flow of FIG. 3A, a plastic substrate 300 is provided and a patterned organic layer 310 is formed on the plastic substrate 300 (Step 30 a). Subsequently an organic/inorganic hybrid layer 315 is coated to the patterned organic layer 310, filling up the openings S of the patterned organic layer 310 and covering the whole surface of the patterned organic layer 310 (Step 30 b), by slot-die coating. Afterwards, a drying step (Step 30 c) is performed to dry up the mixture layer 315. Later, an inorganic layer 320 is coated over the mixture layer 315 (Step 30 d). Such process flow can be repeated several times to form the laminate film, depending on the gas barrier capability required by the products in process. The organic/inorganic hybrid layer is selected from silicon-containing, titanium-containing or aluminium-containing hybrid materials, for example. The organic/inorganic hybrid layer can level the organic layers, and the organic/inorganic hybrid layer has gas barrier capability.

Following the process flow of FIG. 3B, Steps 30 a-30 c are the same as described in FIG. 3A, while in Step 30 d, another organic layer 330 is coated on the mixture layer 315.

Example: Over a transparent polyimide (PI) substrate, an organic acrylate-based photoresist layer of about 1 micron thickness is spin coated to the PI substrate. After soft baking at 90° C., exposure energy 500 mJ/cm² and 220° C. hard baking, a transparent organic layer is obtained. Subsequently, a inorganic layer, made of silicon-containing sol-gel material (IC1-200), of about 300 nm thickness is spin coated over the patterned organic layer and then is dried at 100° C. for 10 minutes and 220° C. for 30 minutes to remove the solvent. Later, another organic acrylate-based photoresist layer of about 1 micron thickness is spin coated to the mixture layer. After soft baking at 90° C., exposure energy 500 mJ/cm² and 220° C. hard baking, another transparent organic layer is formed and the laminate film is obtained. Such gas barrier substrate has water vapour transmission rate (WVTR) value of 10⁻¹ g/m²/day under 25° C. and 60% relative humidity.

The process provided by the present invention preferably applies the totally printing process to fabricate the organic/inorganic multi-layered gas barrier film. As one printing step can achieve patterning and coating at the same time, the process is simplified with lower costs. Through the pattern design (e.g. off-set pattern) of the organic layer and the alternate or complementary arrangement of the patterned organic layer and the adjacent inorganic layer, the inorganic material is interconnected between layers and the vertical diffusion pathway of the gas is elongated, thus improving the gas barrier efficiency. In addition, the continuous inorganic material matrix alleviates the peeling between layers of different materials, further improving the adhesion between the organic and inorganic layers.

By using the totally printable process, it is easier to fabricate large sized gas barrier film for flexible substrates. Moreover, such process can improve the gas barrier capability and flexibility of the substrate for application in flexible touch panel.

Compared with the commonly used vacuum process, the costs for either the applicable materials or the working apparatus/equipments of the present invention are lower.

It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the present invention without departing from the scope or spirit of the invention. In view of the foregoing, it is intended that the present invention cover modifications and variations of this invention provided they fall within the scope of the following claims and their equivalents. 

1. A multi-layered gas barrier laminate film, comprising a flexible substrate, a plurality of organic layers disposed over the flexible substrate and a plurality of inorganic layers disposed over the flexible substrate, wherein the organic layers and the inorganic layers are stacked in alternation, and the inorganic layers are interconnected with one another.
 2. The film of claim 1, wherein each of the plurality of organic layers has a pattern, and the inorganic layers are interconnected with one another through the patterns of the organic layers.
 3. The film of claim 2, wherein the pattern of one organic layer is different to that of another organic layer that is most adjacent thereto.
 4. The film of claim 2, wherein the pattern of one organic layer is arranged off-set to that of another organic layer that is most adjacent thereto.
 5. The film of claim 1, wherein a material of the organic layer is macromolecules or a polymer material with low film-forming temperatures and high light transparency.
 6. The film of claim 5, wherein the organic material with low film-forming temperatures and high light transparency is optical grade polymethylmethacrylate, poly-p-xylene, ethylene-chlorotrifluoroethylene copolymers, fluorinated ethylene-propylene, fluorinated ethers, polytetrafluoroethene, polychlorotrifluoroethylene, polyimide precursor, self-assembly materials or light sensitive materials.
 7. The film of claim 1, wherein a material of the inorganic layer is a sol-gel material.
 8. The film of claim 1, wherein a material of the inorganic layer includes metal oxides or non-metal oxides.
 9. The film of claim 8, wherein the metal oxide is titanium oxide (TiO₂), tin oxide (SnO₂), aluminum oxide (Al₂O₃) or zinc oxide (ZnO), while the non-metal oxide is silicon oxide (SiO₂).
 10. The film of claim 1, wherein a material of the flexible substrate is polyethylene terephthalate (PET), polycarbonate (PC), polymethylmethacrylate (PMMA), polyvinylchloride (PVC), polyimide (PI) or polyethylene (PE).
 11. A totally printable process for forming a multi-layered gas barrier laminate film, comprising: a) providing a plastic substrate; b) printing a first organic layer with a first pattern on the plastic substrate; c) printing a first inorganic layer to the first organic layer, filling up openings within the first pattern of the first organic layer and completely covering a top surface of the first organic layer; d) printing a second organic layer with a second pattern on the first inorganic layer; and e) printing a second inorganic layer to the second organic layer, filling up openings within the second pattern of the second organic layer and completely covering a top surface of the second organic layer.
 12. The process as claimed in claim 11, further comprising repeating the steps of d) to e).
 13. The process as claimed in claim 11, the step b) comprises performing a screen printing process, a doctor blade coating process, a roll coating process, a micro-imprinting process, a spray coating process, a dip coating process, a spin coating process, a flow coating process, a capillary coating process, a chemical coating process or the combinations thereof.
 14. The process as claimed in claim 11, the step c) comprises performing a screen printing process, a doctor blade coating process, a roll coating process, a micro-imprinting process, a spray coating process, a dip coating process, a spin coating process, a flow coating process, a capillary coating process, a chemical coating process or the combinations thereof.
 15. The process as claimed in claim 11, the step d) comprises performing a screen printing process, a doctor blade coating process, a roll coating process, a micro-imprinting process, a spray coating process, a dip coating process, a spin coating process, a flow coating process, a capillary coating process, a chemical coating process or the combinations thereof.
 16. The process as claimed in claim 11, the step e) comprises performing a screen printing process, a doctor blade coating process, a roll coating process, a micro-imprinting process, a spray coating process, a dip coating process, a spin coating process, a flow coating process, a capillary coating process, a chemical coating process or the combinations thereof.
 17. The process as claimed in claim 11, wherein a material of the first organic layers is the same as that of the second organic layers.
 18. The process as claimed in claim 11, wherein a material of the first organic layers is different from that of the second organic layers.
 19. The process as claimed in claim 11, wherein a material of the first inorganic layers is the same as that of the second inorganic layers.
 20. The process as claimed in claim 11, wherein a material of the first inorganic layers is different from that of the second inorganic layers. 